Tear tape with holographic image

ABSTRACT

A substrate, such as the surface of goods or of packaging material for goods, is provided with a security device by applying, to the substrate, a pressure sensitive adhesive tape carrying a security device in the form of a hologram.

This is a continuation of application Ser. No. 08/109,357, filed Aug.20, 1993 abandoned.

This invention relates to tapes and is concerned with tapes for applyingsecurity devices to goods and like articles.

The production and sale of counterfeit goods is an ever-increasingproblem. Such counterfeit goods are frequently packaged so that theyresemble the genuine goods as closely as possible with a view tomisleading the purchaser into believing that genuine goods are beingbought. This causes concern to the manufacturer of the genuine goods.Firstly, the counterfeit sales are sales which ordinarily themanufacturer of the genuine goods could reasonably expect to have made.More importantly, however, the counterfeit goods are often of inferiorquality to the genuine goods and thus their sale can seriously damagethe reputation of the manufacturer of the genuine goods since thepurchaser of the inferior counterfeit goods will ordinarily assume thatthe goods are in fact genuine and will, in future, be less inclined topurchase the genuine goods. Further, in the case where the counterfeitgoods are, for example, replacement brake shoes for a motor vehicle,they may not meet the quality control standards of the manufacturer ofthe original goods and may thus constitute a risk to the safety of theuser.

It is therefore desirable to provide goods or the packaging for goodswith a security device which will act as a guarantee that the goods aregenuine goods. One known form of security device is a hologram.Conventionally, such holograms are applied by means of a hot foilstamping process. In this process, the holograms are formed on a carrierweb provided with a heat activatable adhesive on its underside. Eachhologram is applied to the goods or packaging by stamping it with aheated tool which cuts the hologram from the web, activates theadhesive, and presses the hologram against the surface of the goods orpackaging. The process is relatively slow and therefore expensive.

It is known to provide cards or tickets with magnetic informationrepresenting monetary value such as, for example, phone cards fortelephone services and tickets for transport services. The cards ortickets are normally prepaid and, when used to pay for the serviceassociated therewith, they are read by an appropriate machine whichdetermines whether or not the monetary value of the card is appropriateto the service required and, if it is, the service is provided. Themagnetic information may be in the form of a magnetic strip carried by asupport of, for example, card or plastics material. It is desirable toprovide such cards or tickets and indeed other articles carryingmagnetic information, such as credit cards, with a security device toprevent fraudulent use. However, as indicated above, there aredifficulties in applying holographic security devices.

It is one object of the present invention to provide a simple techniquewhereby holograms may be applied to goods and other substrates.

According to one aspect of the present invention there is provided atape for applying to a substrate, to attach a security device to thesubstrate, which tape is formed from an oriented base film ofthermoplastic plastics material coated with a pressure sensitiveadhesive composition on one surface and with a release agent on anothersurface and including a security device in the form of a hologram.

By providing the hologram on a tape in this way, the hologram can bereadily applied to the substrate by moving the tape and substrate alongconverging paths and then affixing the tape to the substrate by means ofthe adhesive.

Accordingly, another aspect of the present invention provides a methodof attaching a security device to a substrate which comprises:

(i) providing a continuous tape as above defined,

(ii) causing the substrate to move along a substrate path,

(iii) moving the tape along a tape path,

(iv) bringing the paths together, and

(v) affixing the tape to the substrate by means of the adhesive

The present invention is described with reference to the accompanyingdrawings, in which:

FIG. 1 is a diagrammatic cross-sectional view through a tape applied toa substrate in accordance with the present invention; and

FIG. 2 is a plan view of a ticket including a tape in accordance withthe present invention.

In an embodiment, the substrate is packaging material of, for example,plastics material film or card or fibre board or corrugated board, forenveloping goods to form a package. In this case, the tape may functionas a tear tape to facilitate the opening of the package. Moreparticularly, it will generally have a free end which can be gripped bythe opener and, when pulled, tears through the packaging material toenable access to be gained to the goods inside the package. In addition,however, the hologram incorporated in the tear tape serves as a securitydevice and enables the recipient of the package to ascertain whether ornot the packaging material and tear tape have been applied by anauthorised person and hence whether or not the goods in the package aregenuine goods. The recipient merely needs to ascertain whether or notthe tear tape includes an authentic hologram as used by the originalmanufacturer or other authorised person. If the tear tape includes nohologram at all, then the recipient knows that the goods are not genuinegoods. Similarly, if the tear tape includes a hologram which is not ofthe type used by the authorised person, then again he knows that thegoods are not genuine.

In another embodiment, the substrate may be a shrink sleeve or a shrinkcollar provided on an article to prevent tampering with the article,with the tape acting as a security device to provide an indication ofattempts to remove and replace the sleeve and also, optionally, actingas a tear tape for the sleeve or collar to facilitate opening. In thelatter case, the tape is preferably disposed on the shrink sleeverelatively to perforations in the sleeve such that the tape splits as ittears the sleeve. In this way the tape is damaged and cannot be put tofraudulent re-use.

In a further embodiment, the substrate may be a label, for example, ashrink label, denoting authenticity, with the tape acting as a securitydevice indicating that the label has not been removed and replaced. Inthese cases also, by examination of the hologram the recipient of apackage incorporating a tape in accordance with the invention canreadily ascertain whether or not the tape is of the type applied by themanufacturer of the genuine goods or some other authorised person.

The tape may also be directly applied to the goods themselves (insteadof to the packaging material therefor) in the case where the goods arecontainers of, for example, expensive products such as brandy.

In a further embodiment, the substrate may be a sheet of plasticsmaterial or card carrying or intended to carry machine readable magneticinformation representing, for example, a monetary value with thehologram of the tape providing the substrate with a security device toprevent fraud. In this case, in order to facilitate the stacking of aplurality of such sheets, it is preferred for each sheet to include twotapes at opposite ends of the sheet (on the same surface of the sheet oron opposite surfaces). In this way, a more stable stack of sheets isobtained.

The magnetic information may, for example, be a magnetic image formed ina layer of a magnetisable composition based upon ferric oxide or chromicoxide. Such compositions are, however, coloured and it may be preferredfor the magnetisable composition to be colourless. Colourlessmagnetisable compositions are known and may comprise, for example, atransparent colourless plastic matrix containing a particulatecrystalline magnetisable dispersed phase having a matching refractiveindex. The dispersed phase may comprise a colourless ferromagnetic atomsuch as a rare earth element (e.g. gadolinium), a refractory metal oxidesuch as titanium oxide, an inorganic fluoride such as calcium fluoride,and a glass such as an inorganic borate, phosphate, oxide or fluoride.The plastic matrix may be, for example, polyvinyl chloride or an acrylicpolymer.

In the case where the tape is applied to filmic packaging material orother non-rigid packaging material such as fibre-board or card, it ispreferred for it to be applied using a tape dispenser including amotorised reel for the tape in accordance with our EPB-0121371. In thisway tension imbalance between the tape and the packaging material isreduced by controlling the speed of movement of the tape in dependenceon the speed of movement of the packaging material by increasing therotational speed of the reel when the tension in the tape increases andby decreasing the rotational speed of the reel when the tension in thetape decreases. Alternatively, in the case where the substrate iscorrugated board or other relatively non-extensible material, the tapemay be applied using non-motorised tape dispensers.

In the case where the substrate is fluted board, the tape may bethreaded and secured between the fluting and the inner or outer liner sothat it is not readily visible so as to provide the substrate with acovert security device.

Preferably the tape is produced in the form of traverse wound reelscontaining from, for example, 3000 to 60000 linear metres.

The base film of the tape, which may be in the form of a laminate, mayfor example have a thickness of from 10 to 100 μm and a width of from 1to 20 mm. Preferably, the thickness is from 20 to 70 μm and the width isfrom 1.5 to about 15 mm.

The plastics material of the base film is oriented so as to reduce itsextensibility and to enable thinner tape to be produced and it may beoriented either monoaxially or biaxially. Any thermoplastic plasticsmaterial may be used for the base film provided that it is sufficientlydimensionally stable in the cross-direction to facilitate accurateslitting of sheets of the material to form the tape. Also, the plasticsmaterial needs to be metallisable unless it is coated with a primerreceptive to metallisation. It is particularly preferred for thethermoplastic plastics material to be formed from monoaxially orientedpolypropylene or from biaxially oriented polyester or polyesterlaminate. The hologram may be applied to one surface of the base film orit may be sandwiched between two base films.

Any suitable pressure sensitive adhesive composition may be used. Thus,it may, for example, be based on natural or synthetic rubber or onacrylic compounds and normally a primer coating will be provided betweenit and the surface of the base film so as to promote anchorage of thepressure sensitive adhesive composition. That surface of the base filmwhich is not coated with the pressure sensitive composition is coatedwith a release agent such as a silicone release lacquer.

A wide variety of holographic images can be incorporated to provide thedesired security device. For example, they may be in the form of spiralsin one or other direction or a combination of the two. Moreover, theymay exhibit a sequence of colours. The holograms which are in the formof two dimensional images, three dimensional images, or a combination ofboth. Further, the hologram may have different levels of security builtinto it. Thus, it may comprise an overt security device having an imagevisible to the naked eye and/or a covert security device having an imagewhich is quasi visible or invisible to the naked eye. (Quasi visibleimages are images which include deliberate errors which are not readilyapparent on inspection with the naked eye and which are included inorder to assist in the detection of copying). More particularly thehologram may incorporate invisible images which can only be constructedby viewing the hologram at particular angles or under special lightconditions using specialist scanning equipment. In the case where thehologram includes a visible image, it may represent, for example, amonetary value or a trade mark in addition to serving as a securitydevice.

Ordinarily, the holograms may be manufactured using embossing techniquesto produce a plurality of longitudinally extending holographic imagesacross the surface of a web of the base film material and this web isthen slit to form a plurality of tapes with each tape including one ofthe longitudinally extending holographic images. Before slitting theweb, it is ordinarily coated with both a primer and the pressuresensitive adhesive composition on one surface and with the release agenton the other. In the case where the tape is to be used as a tear tapefor transparent filmic packaging material, the pressure sensitiveadhesive composition will be transparent and coated on to that surfaceof the web which carries the holographic image in right-reading form sothat the image can be seen through the composition and the filmicpackaging material. In the case where the tape is to be applied to alabel, or other non-transparent substrate, the base film.of the tapewill generally be provided with the hologram in wrong-reading form priorto overcoating with the pressure sensitive adhesive.

Preferably the holograms are tamper-proof or tamper-evident. Thus, forexample, that part of the tape carrying the hologram may be providedwith score lines or perforations so that the tape will rupture and notpull off in one piece from the substrate if attempts are made totransfer the tape to another substrate.

The tapes of the invention are useful for applying holographic securitydevices to packages of cigarettes, perfumes, spirits and other highvalue duty free goods; to packages of car parts, computer software, andpharmaceuticals; to FMCG (fast moving consumer goods); and to ticketsand cards.

The Following Example Illustrates the Invention

EXAMPLE 1

Referring to FIG. 1, a film 1 of monoaxially oriented polypropylenehaving a thickness of about 40 μm was formed in conventional manner. Onesurface of the film was then primed with a primer 2, coated withembossing lacquer 3 and embossed to form a plurality of longitudinallyextending right-reading holographic images 4 in the surface in theconventional manner. The imaged surface was then coated with aluminium5. It was subsequently coated with a primer 6 and a transparent pressuresensitive adhesive composition 7. The primer was a solution in tolueneof 25 parts of natural crepe rubber and 8 parts of a cross-linking agent(Vulcabond TX) to give a coating weight of 0.25 gms per square metre.Vulcabond TX is manufactured by ICI and is a 50% solution ofpolyisocyanate (mainly diphenyl methane di-isocyanate) in xylene. Thepressure sensitive adhesive composition was a solution of 100 partsnatural crepe rubber, 110 parts of a tackifying resin having a meltingpoint of 110/115° C. (Arkon P) and one part of an oxidant (Irganox)dissolved in a hydrocarbon mixture (SBP2). This was applied by aconventional reverse role coating technique to give a dry coating weightof 15 to 20 g/m². Arkon P is marketed by Arakara Chemicals and is afully saturated cyclic hydrocarbon resin and Irganox is marketed byCiba-Geigy and is a high molecular weight bonded polyphenol.

The non-imaged surface of the web was then coated with a release agent 8comprising 100 parts of Silcolease 425 (a 30% solids concentration ofdimethyl polysiloxane and methyl hydrogen polysiloxane resins in toluenefrom Rhone Poulenc) together with 4 parts of Catalyst 62A and 4 partsCatalyst 62B (50% solids concentration of aminoalkoxy-polysiloxane intoluene and alkyl tin acrylate in xylene, respectively from RhonePoulenc). It was applied to give a dry coating weight of 0.25 g/m².

The thus coated film was then slit longitudinally in registry with thelongitudinally extending holographic images so as to provide a pluralityof pressure sensitive tear tapes of width 3 mm and each including aholographic image extending continuously longitudinally of the tape. Theresultant tape was then traverse wound onto centres of internal diameter150 mm and widths 170 mm to provide reels carrying continuous lengths oftape about 50,000 metres long.

The tear tape was subsequently fed from the-reel along a path convergingwith the path of moving polypropylene packaging film 9, so as to beadhered thereto by the adhesive, in a film overwrapping machine toproduce a plurality of packages each including a tape which is fortearing the overwrapping film by the end user and which carries asecurity device in the form of a hologram. The holographic image on thetear tape served as an indication of the authenticity of the goods inthe packages.

EXAMPLE 2

Referring to FIG. 2, a biaxially oriented polyester film was preparedand provided with wrong-reading holographic images in the manner ofExample 1. The holographic images included overt images and covertimages which were machine readable. The imaged surface was coated with aprimer and pressure sensitive adhesive composition and the other surfaceof the film was coated with a release agent. Thus the images wereright-reading when viewed through the release agent coating.

The pressure sensitive adhesive composition was a 45% solids solution ofa self cross-linking acrylic polymer in a mixture of 37 parts ethylacetate, 26 parts heptane, 26 parts isopropanol, 1 part toluene and 1part acetylacetone. This is commercially available as 180-1054 fromNational Starch Corporation. The primer was a mixture of 100 parts ofthe aforesaid 180-1054, 1400 parts of toluene, and 10 parts of theaforesaid Vulcabond TX. The release agent comprised 20 parts of Syloff7046, 79.9 parts of toluene and 0.1 part of a reactive siloxane polymerknown as catalyst/cross linking agent 7048 (Dow Corning). Syloff 7046 isa mixture of reactive siloxane polymers available from Dow Corning.

The coated film was slit to form a tape 20 of 2 mm width and the tapewas traverse wound onto centres of internal diameter 29 mm and widths of85 mm to provide reels of continuous tape of about 7000 metres long.

A web of card 21 was coated with a magnetisable composition to form amagnetic strip 22 extending along the web. The tape was fed, from thereel, along a path converging with a path along which the web of cardwas moving so as to be affixed to the web by the adhesive. The web wasthen cut into a plurality of separate tickets 23, each of which includeda magnetic strip and, at opposite ends of the ticket, a length of thetape provided with a hologram. During this cutting operation, aplurality of score lines 24 was simultaneously provided transverselyacross the tape in the region of the hologram. The magnetic strip ofeach ticket was then encoded so as to represent a monetary value.

The tickets could be used to obtain services appropriate to the monetaryvalue represented by the magnetic strip as determined by means of asuitable reader machine. The hologram served as a security device toprevent fraudulent use of the tickets.

What is claimed is:
 1. A self-wound, tear tape for applying to asubstrate to attach a holographic image to the substrate, which tapecomprises; an oriented base film of thermoplastic plastic material andhaving first and second surfaces, a release agent coated on the surfaceof the base film, a holographic image on the second surface of the basefilm inseparable therefrom, and a pressure sensitive adhesivecomposition coated over the holographic image.
 2. A tape as claimed inclaim 1, wherein the thermoplastic plastic material is selected from thegroup consisting of monoaxially oriented polypropylene and biaxiallyoriented polyester.
 3. In combination: (i) a self-wound, tear tape whichcomprises an oriented base film of thermoplastic plastic material andhaving first and second surfaces, a release agent coated on the firstsurface of the base film, a holographic image on the second surface ofthe base film inseparable therefrom, and a pressure sensitive adhesivecomposition coated over the holographic image; and (ii) a substrate towhich the tape is adhered by said adhesive.
 4. A combination as claimedin claim 3, wherein the substrate is selected from the group consistingof packaging film and cardboard.
 5. A combination as claimed in claim 3,wherein the holographic image is provided with score lines.
 6. Acombination as claimed in claim 3, wherein the substrate additionallyincludes a layer of a magnetizable composition.
 7. A combination asclaimed in claim 3, wherein the holographic image is provided withperforations.
 8. A combination as claimed in claim 3, whereby thesubstrate is selected from the group consisting of a shrink sleeve, ashrink collar and a label.